Waterkol D is an one-component adhesive manufactured on the basis of hydrous vinyl dispersion with the addition of extender and modifying agents.
Characteristics of adhesive:
Colour: white
Viscosity acc. to CF Ø 10 mm: 20 - 50 s
Dry residue: 45-54 %
pH: 5 - 7
Time of pressing: 15 minutes
Working temperature: 18 - 25 °C
Initial shearing resistance of adhesive-bonded joint: min. 2,8 MPa
Total shearing resistance of adhesive-bonded joint: min. 8,8 MPa
Basic assembling adhesive. The adhesive is designed for cold bonding of:
- hard and soft wood,
- chipboards, plywood and other wood-based materials with paper, fabric or plastic veneers
|
Powrót na górę
|
|
|
|
|
|
|
|
|
|
Waterkol DW is an one-component adhesive manufactured on the basis of hydrous vinyl dispersion with the addition of modifying agents. The adhesive is distinguished by high resistance of adhesive-bonded joint in D3 class and high thermal resistance of up to 70°C.The adhesive is designed for cold bonding of:
- hard and soft wood,
- chipboards, plywood and other wood-based materials
- for veneering wood and wood-based surfaces with scaleboard and paper, fabric or plastic slats.
- wood and wood-based elements exposed to short-term effects caused by cold water or drips, or to long-term effects caused by high air humidity, e.g.: kitchen and bathroom furniture, doors, windows, railings,
- for postforming pressure cycle,
- composite boards with the use of a press.
Colour: white
Viscosity acc. to CF Ø 10 mm: 15 - 50 s
Dry residue: 45-54 %
pH: 5 - 7
Class of waterresistance: D3
Time of pressing: 15 minutes
Initial shearing resistance of adhesive-bonded joint: min. 2,8 MPa
|
|
Powrót na górę
|
|
|
|
|
|
|
|
|
|
Waterkol DS is an one-component adhesive manufactured on the basis of hydrous vinyl dispersion with the addition of modifying agents. The adhesive is distinguished by its short setting time and high thermal resistance of adhesive-bonded joint.
Colour: white
Viscosity acc. to CF Ø 10 mm: 15 - 50 s
Dry residue: 45-54 %
pH: 5 - 7
Shearing resistance of adhesive-bonded joint: cold bonding
initial after 10 minutes: min. 3,0 MPa
final after 24 hours: min. 9.0 MPa
Bonding at temperature of 70°C
initial after 10 minutes: min. 3,0 MPa
final after 24 hours: min. 9.0 MPa
Total shearing resistance of adhesive-bonded joint: min. 9,0 MPa
BONATEX DS adhesive is a quickly bonding adhesive designed to bond:
- block-bonding of hard and soft wood in presses heated by high-frequency currents,
- large surfaces of wood and wood-based materials,
- assembly and edgy elements,
- composite boards with the use of a press.
|
|
Powrót na górę
|
|
|
|
|
|
|
|
|
|
Bonasol SW is a special solvent adhesive based on rubber modified with synthetic resins.
Dry residue [%], minimum:44 ± 2% according to PN-EN 827
Viscosity CF Ø 4 mm, outflow 50 cm3[s]: 90
Surface soundness measured after 24 hours: manually, for joints: polyurethane foam with polyurethane foam - higher than foam resistance
Open time: one-sided - to 3 minutes, two-sided - 30 minutes
Bonasol SW is designed for industrial applications especially for bonding fabric made of poliester,cotton, cellulose among each other as well as to wood, hardboard, chipboard. Mainly use in upholstery and automotive industry. Adhesive can be applied on one or two joined surfaces.
|
|
Powrót na górę
|
|
|
|
|
|
|
|
|
|
Bonatap M38 is an adhesive manufactured on the basis of styrene-butadiene rubber and synthetic resin in organic dissolvent. Having dried, the adhesive gives as a soft elastic joint which does not result in foam shrinking.
Dry residue [%], minimum:38 ± 2% according to PN-EN 827
Viscosity CF Ø 4 mm, outflow 50 cm3[s]: 30 - 40
Surface soundness measured after 24 hours: manually, for joints: polyurethane foam with polyurethane foam - higher than foam resistance
Joint shrinkage: does not occur
BONATAP M38 adhesive is designed mostly for the furniture industry to bond upholstery materials, such as polyurethane foam, fabric, wood, textiles etc.
|
|
Powrót na górę
|
|
|
|
|
|
|
|
|
|
Bonatap M50 BTV is a solvent-base adhesive based on styrene-butadiene rubber and synthetic resin. Itgive after drying soft and elastic bond, and not cause foam shrinkage. BONATAP M50 BTV can be used for one-side spray application as well as two-sided application. It have very little odour.
Specification of the adhesive:
Appearance: viscose, light yellow or dark pink liquid
Solid content: 50±3% according to PN-EN 827
Viscosity: Viscosity (Ford Cup 4mm, outflow 50 cm3): : 30-45 sec. according to PN-EN ISO 2431, Viscosity Brookfield LDVD: about 320 mPa.s
Open time for:one-sided spraying about 1-5 minutes, Two-sided spraying about 10-15 minutes
Joint shrinkage:not occur
Areas of Application: BONATAP M50 BTV is designed for upholstery industry mainly to joining of upholstery materials like
polyurethane foams, textiles, wood, fabrics, etc. BONATAP M50 BTV give soft and elastic joint.
|
|
Powrót na górę
|
|
|
|
|
|
|
|
|
|
Bonatap M50 BTV plus is a solvent-base adhesive based on styrene-butadiene rubber and synthetic resin. It give after drying soft and elastic bond, and not cause foam shrinkage. BONATAP M50 BTV plus
can be used for one-side spray application as well as two-sided application. It have very little odour.
Specification of the adhesive:
Appearance: viscose, light yellow or dark pink liquid
Solid content: 50±2% according to PN-EN 827
Viscosity: Viscosity (Ford Cup 4mm, outflow 50 cm3): : 30-45 sec. according to PN-EN ISO 2431, Viscosity Brookfield LDVD: about 320 mPa.s
Open time for:one-sided spraying about 1-5 minutes, Two-sided spraying about 1-15 minutes
Joint shrinkage:not occur
Areas of Application: BONATAP M50 BTV plus is designed for upholstery industry mainly to joining of upholstery materials like
polyurethane foams, textiles, wood, fabrics, etc. BONATAP M50 BTV PLUS give soft and elastic joint.
|
|
Powrót na górę
|
|
|
|
|
|
|
|
|
|
Bonatap M61 is a solvent-base adhesive based on styrene-butadiene rubber and synthetic resin. It give after drying soft and elastic bond, and not cause foam shrinkage. BONATAP M61 can be used for one-side spray application as well as two-sided application. It have very little odour.
Specification of the adhesive:
Appearance: viscose, light yellow or dark pink liquid
Solid content: about 60 ±2% according to PN-EN 827
Viscosity: Viscosity (Ford Cup 4mm, outflow 50 cm3): : at least 60 sec. according to PN-EN ISO 2431, Viscosity BrookfieldLDVD: 700-800 mPa.s
Open time for: one-sided spraying about 1-6 minutes, Two-sided spraying about 1-20 minutes
Joint shrinkage: not occur
Areas of Application: BONATAP M61 is designed for upholstery industry mainly to joining of upholstery materials like polyurethane foams, textiles, wood, fabrics, etc. BONATAP® M61 give soft and elastic joint.
|
|
Powrót na górę
|
|
|
|
|
|
|
|
|
|
Waterkol MT it is high quality water-based polychloroprene adhesive. This adhesive not contain any solvents. It is incombustible and non-toxic. Waterkol MT is particularly attractive, fully safe alternative for sol vent-based adhesives used to bonding of upholstery materials especially.
Specification of the adhesive:
Appearance: a milky-white or rose-colored liquid
Solid content: 55 ± 3%
Viscosity: Viscosity Brookfield LDVD, PN ISO 2555:300 ± 100 mPa.s
Peel strength according to PN-ISO 11339, material PU foam-PU foam:higher than foam strength
Boiling point: 100oC
Freezing point: 0oC
Heat resistance of adhesive bond: 100oC
The joint made from Waterkol MT has high flexibility.
Areas of Application: Waterkol MT is designed for gluing of foams as polyurethane, latex to textiles, polyester fibre, jute, wood, chip board,
cardboard, mineral wool, metal plates, polystyrene and others. Waterkol® MT is especially designer for furniture,packing, automotive industry and others, where foam or other porous materials are commonly used.
|
|